MX2000-1 Graphite Embedded Alloy Bearing

MX2000-1 graphite embedded alloy bearing, MX2000-1 graphite scattered alloy bearing is an improved product of JF800 bimetallic bearing. It has the pressure resistance and wear resistance of JF800 bimetallic bearing, and achieves oil-free lubrication after graphite scattered. The friction coefficient is small under the condition of no oil or little oil, and the phenomenon of shaft biting is completely prevented. This product is suitable for the guide parts of rubber tire molds, the sliding parts of lifting equipment, the high-speed sliding parts of turbines and other places with high temperature, high speed and cannot be refueled for a long time.

Dapatkan Penawaran

PREV：MX2000-2 Nickel-Graphite Dispersed Alloy Bearing NEXT：No next article

perkenalan produk
Parameter
Deskripsi Bahan
Hubungi kami

Fitur Produk

1 Dapat bekerja untuk waktu yang lama dalam kondisi bebas minyak.

2 Lebih cocok untuk kondisi kerja kecepatan rendah dan beban berat, dengan ketahanan aus yang baik dan gesekan yang sangat rendah.

3 Cocok untuk situasi dimana lapisan oli sulit terbentuk, seperti bolak-balik, berputar dan gerakan intermiten.

4 Tahan terhadap korosi dan oksidasi.

5 Bebas perawatan dan masa pakai yang lama.

Mengapa Memilih Bantalan Tanpa Minyak

Mengurangi biaya Manufaktur

Tidak diperlukan perangkat suplai oli, lubang injeksi oli, atau oli pemrosesan alur, yang dapat sangat menghemat biaya produksi.

Mengurangi Biaya Operasional

Ini sangat mengurangi penggunaan minyak pelumas, mengurangi pemeliharaan peralatan, dan menghindari bahaya tersembunyi yang disebabkan oleh pasokan minyak yang tidak mencukupi, sehingga secara efektif mengurangi biaya operasional.

Mempersingkat Waktu Desain

Desain bebas minyak menyederhanakan struktur produk dan secara efektif menghemat waktu desain. Kami profesional Pemasok ODM dari MX2000-1 Graphite Embedded Alloy Bearing

Kondusif Terhadap Perlindungan Lingkungan

Tidak diperlukan daur ulang limbah minyak, yang juga bermanfaat bagi perlindungan lingkungan.

Bidang Aplikasi

Suhu tinggi

·Pabrik baja

·Tungku peleburan

·Peralatan pengeringan

·Oven pemanggang

· Pengontrol panas

Tahan air

·Gerbang bendungan

·Pompa air

·Struktur saklar fluida

·Struktur lepas pantai

·Peralatan mesin dermaga dan lumpur

Industri kimia

·Pabrik kimia

·Peralatan elektroplating

·Peralatan pengolahan air limbah

·Mesin pencelupan

·Peralatan penyulingan minyak dan kimia

Energi

·Tenaga angin

·Energi baru

Mengirimkan

· Derek dek

·Jangkar

· Penutup palka

·Lengan kemudi

·Mesin pengangkat dan peralatan cincin pengangkat

Manufaktur Mobil

·Cetakan stempel

·Struktur pengelasan

· Pengecatan dan pengeringan garis

· Sabuk konveyor logam

·Peralatan mesin

Industri berat

·Mesin pabrik pipa baja

·Pabrik ban dan kertas

·Pembangkit listrik

·Menghubungkan sakelar mesin injeksi cetakan

Konstruksi, Penambangan, Pemuatan

·Mixer, penggiling, penghancur

·Mesin konstruksi

·Peralatan pertambangan

·Bantalan batang penghubung

Jembatan dan Rel Angkat

· Bantalan jembatan

·Balok, jembatan, jembatan gantung

·Reaktor yang berhubungan dengan energi nuklir

·Generator uap

Copper alloy material	CuSnPb+C	Maximum operating temperature	300℃
Maximum bearing pressure	20N/mm²	Friction coefficient μ	0.05~0.18

MX2000-1 is a dual alloy self-lubricating bearing material consisting of a sintered layer as a sliding wear-resistant material and a metal matrix as a bearing load support. The sintered layer is composed of a special copper alloy material evenly distributed in graphite and PTFE solid lubricants. When microscopic movement occurs, it can easily form a firm solid transfer film. This film has a very low friction coefficient and low shear strength, and can adhere to the surface of the mating part even under heavy load conditions. The metal substrate provides good mechanical strength and dimensional stability. Carbon steel, copper-based materials and other materials can be selected according to the operating conditions, or surface coating can be performed to improve corrosion resistance.

Features

●Can be used for a long time without maintenance;

●Designed for high static and dynamic loads;

●Has a very low and stable friction coefficient, no adhesion;

●Has dust resistance, corrosion resistance, impact resistance and edge load resistance;

●Has good electrical and thermal conductivity;

●Can be used in a wide temperature range;

●Suitable for occasions such as reciprocating, rotating and swinging where the start-up is frequent and it is difficult to form an oil film;

●Has an extremely low wear rate and a long service life;

●Can be reprocessed after installation to obtain higher tolerances;

●Can be used under vacuum.

Technical Parameters

Material Name		MX2000-1#1	MX2000-1#2	MX2000-1#3	MX2000-1#4
Metal Matrix		Carbon Steel	Carbon Steel	Stainless Steel	Bronze
Wear-resistant Layer	Ingredients	CuSn12+SL	CuSn10Pb10+SL	CuSn12+SL	CuSn12+SL
	Solid lubricant	6%	6%	6%	6%
	Hardness HB	>40	>40	>40	>40
	150Mpa Compression deformation mm	<0.005	<0.005	<0.005	<0.005
Maximum load	Static load N/mm²	150	120	150	150
Maximum load	Dynamic load N/mm²	100	80	100	100
Maximum linear speed m/s		0.5	0.5	0.5	0.5
Maximum PV value N/mm²*m/s		1.5	1.5	1.5	1.5
Friction factor μ		0.05~0.2	0.03~0.2	0.05~0.2	0.05~0.2
Operating temperature ℃		-195~+280	-195~+280	-195~+280	-195~+280

Wear-resistant Layer

The standard MX2000-1 material surface is in the form of a smooth plate. At the same time, oil grooves can be processed according to customer needs to effectively drain the abrasive particles generated during the operation of the bearing, foreign matter or impurities intruded from the external environment, etc. In addition, regular oil storage holes can be processed according to needs. Under special working conditions, in order to reduce the initial friction coefficient, low-friction materials such as PTFE or molybdenum dioxide can be sprayed on the surface of the wear-resistant layer.

Typical applications

The characteristics of MX2000-1 material can meet the needs of many occasions where oiling or lubrication is not possible, such as turbines, guide vane dam working doors and accident doors, injection molding machines, packaging machinery, tire molds, industrial furnaces, vacuum equipment, papermaking equipment, and radiation-exposed workplaces.

Komposisi dan Sifat Bahan
Material	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
Kepadatan	8.0	8.9	7.8	8.9	8.0
Kekerasan HB	>210	>70	>150	>95	>250
Kekuatan Tarik N/mm²	>750	>200	>600	>260	>800
Kekuatan Hasil N/mm²	>450	>90	>260	>150	>450
Pemanjangan%	>12	>15	>10	>৪	>800
Koefisien Ekspansi Linier 10 ^-5 /℃	1.9	1.8	1.6	1.8	1.9
Batasi Suhu ℃	-40~ 300	-40~ 400	-40~ 400	-40~ 400	-40~ 150
Maks. Muat N/mm²	100	60	50	70	120
Maks. Kecepatan (Kering) m/mnt	15	10	20	10	15
Maks.PV N/mm²*m/mnt	200	60	60	80	200
Kompresi Deformasi Permanen 300N/mm²	<0,01	<0,05	<0,04	<0,05	<0,05
*Permintaan besar dengan bahan khusus tersedia.

Pertukaran Bahan Dasar
Kode Bahan	Merek Cina GB1176-87	Internasional ISO 1338	Jerman KERIUHAN	Jepang JIS	Amerika ASTM (UNS)	Inggris BS	Italia JM	Ketentuan yang berlaku
Perunggu Pengecoran JDB	ZCuZn25AI5 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 Bab 86300	HTB2	JM18-1	Beban tinggi, kecepatan rendah Biasa digunakan
JDB-1Perunggu	ZCuSn5 Pb5Zn5	GCuPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 SM6	B30-92 Bab 83600	LG2	JM7-15	Beban sedang, kecepatan rendah Biasa digunakan
JDB-2Perunggu	ZCuAI9Fe4 Ni4Mn2	GCuAI10 FeNiS	DIN17656 G-CuAI10Ni	H5114 AIBC3	B30-92 Bab 95500	AB2	JM3-15	Beban sedang, kecepatan sedang, Biasa digunakan
JDB-3Perunggu	ZCuSn12		G-CuSn12	CAC503B	B30-92 Bab 90800	PB2	JM1-15	Beban sedang, kecepatan rendah, Biasa digunakan
JDB-5	ZCuZn25AI6 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 Bab 86300	HTB2	JM18-1	Pada beban tinggi, kecepatan rendah, beban tinggi digunakan

Pelumas Padat
Pelumas	Fitur	Aplikasi khas
SL1 Tambahkan grafit	Ketahanan yang sangat baik terhadap bahan kimia serangan dan gesekan rendah, batas Temp 400 ℃	Cocok untuk mesin umum dan di bawah atmosfer
SL4 PTFE menambahkan	Gesekan terendah dan Pelumasan air yang baik, Batas suhu 300℃	Kapal, turbin hidrolik, turbin gas, dll.

SUBMIT

Tentang kami

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. sebelumnya dikenal sebagai Pabrik Mesin Presisi Jiashan Mingxu, didirikan pada tahun 2011. Perusahaan ini berlokasi di pedalaman Zona Demonstrasi Pengembangan Terpadu Delta Sungai Yangtze, dengan lokasi dan transportasi yang nyaman. Dengan lebih dari sepuluh tahun pengalaman manufaktur dan penelitian dan pengembangan, perusahaan ini telah terlibat secara mendalam dalam pengembangan dan produksi bantalan pelumas padat, skateboard, slideways, dan slider. Pemasok ODM dan Perusahaan Bantalan Pelumas Mandiri Bertatahkan Grafit Flange Bushing Bahu JFB di Cina. Pembuatan produk mengadopsi peralatan otomasi modern, secara ketat menerapkan standar sistem manajemen mutu ISO2000, dan proses utama diproses oleh mesin CNC presisi tinggi. Produk utama perusahaan mencakup serangkaian produk seperti bantalan pelumas mandiri bertatahkan padat JDB, bantalan sinter baja-tembaga, bantalan pelumas mandiri SF-1, bantalan pelumas mandiri batas SF-2, dan bantalan tembaga FB090. Banyak digunakan dalam industri otomotif, mesin konstruksi, peralatan metalurgi, mesin pertambangan, cetakan injeksi, cetakan, tekstil, percetakan dan banyak bidang manufaktur mesin lainnya; Hingga saat ini, produk perusahaan telah tersebar di seluruh China dan diekspor ke banyak negara asing, serta sangat dikenal dan dicintai oleh pelanggan dalam dan luar negeri. Mingxu Machinery menganut prinsip layanan "layanan berkualitas tinggi yang berorientasi pada kualitas", dan berusaha keras untuk menyediakan produk dan layanan profesional kepada pelanggan. Pasokan Grosir Bantalan Pelumas Mandiri Bertatahkan Grafit Flange Bushing Bahu MXB-JFB. Perusahaan akan terus memperkenalkan talenta, meningkatkan mekanisme manajemen, integritas, pengembangan, inovasi, dan berupaya membangun merek kelas dunia.